The alloys studied have important differences in chemical composition, mainly in the molybdenum and copper content, which mainly determine its microstructure. The results showed an increase in the hardness of both alloys with decreasing treatment temperature; which is due to the fact that the amount of retained austenite transformed to martensite increases as the martensite finish temperature (Mf) is reached. It was also observed that a higher molybdenum content produces a metastable austenitic matrix in the as cast samples. Furthermore, the effect of Mo and other alloying elements substantially stabilizes the austenite, obtaining low amounts of martensite after the sub-zero treatment, even at -180 degrees C.