A kinetic study of the cobalt electrodeposition onto a carbon fiber ultramicroelectrode of 11 mu m of diameter was conducted in overpotential conditions from an aqueous solution containing 0.01 M CoCl2 + 0.1 M NH4Cl. From the voltamperometric and chronoamperometric studies, it was found that the value of the diffusion coefficient is 1.2x10(-5) cm(2) s(-1). The analysis of the current density transients suggests that cobalt electrodeposition onto a carbon fiber electrode follows an instantaneous nucleation process controlled by spherical diffusion mass transport. Also, the number of active nucleation sites increases as the applied potential decreases.